Cell phone：+82-010-3146-3890；E-mail：geumyangmaterials@naver.com；
420 SS ( STS SUS ) Wire
420 스테인리스 스테인 와이어
ss420 sts420 sus420 wire
사진 설명을 입력하세요.
Product Introduction
Cr13 is a 420 ( SS STS SUS ) stainless steel wire, specifically designed for arc spray processes. TANKII Cr13 forms a dense, well bonded coating, with excellent wear resistance and good corrosion resistance. It is widely used for machine elements repair, dimensional restoration, and wear resistant application. TANKII Cr13’s low shrink rate characteristics allows for increased coating thickness on parts requiring heavier coatings.
Chemical Content %
|
Nominal Composition
|
Cr%
|
Si%
|
Mn%
|
C%
|
Fe%
|
|
--
|
13.0
|
1.0
|
1.0
|
0.3
|
Bal.
|
Mechanical Properties
|
Property Name
|
Value
|
|
Abrasion Resistance
|
Excellent
|
|
Corrosion Resistance
|
Good
|
|
Typical Hardness
|
HRC 40-45
|
|
Bond Strength
|
7100 psi
|
|
Deposit Rate
|
10 lbs/hr/100A
|
|
Deposit Efficiency
|
70%
|
|
Wire Coverage
|
0.8 oz/ft2 / mil
|
|
Coating Shrink
|
Rate Low
|
|
Service Temperature
|
Up to 550C 1022 F
|
Size & Packaging
|
Condition
|
Solid wire
|
|
Diameter
|
1.6mm(14 ga), 2.0mm, 3.175mm
|
|
Package Size
|
10kg, 15kg, or up to client's demand
|
제품 소개
Cr13은 아크 스프레이 공정을 위해 특별히 설계된 420 스텐레스 강선입니다. TANKII Cr13 코팅와이어은 내마모성이 우수하고 내 부식성이 우수한 치밀하고 잘 결합 된 코팅을 형성합니다. 그것은 널리 기계 요소 수리, 차원 복원 및 내마 모성 응용 프로그램에 사용됩니다. TANKII Cr13의 저 수축율 특성은보다 무거운 코팅이 필요한 부품의 코팅 두께를 증가시킵니다.
화학 물질 함량 %
|
명목상의 구성
|
Cr %
|
Si %
|
Mn %
|
C %
|
Fe %
|
|
-
|
13.0
|
1.0
|
1.0
|
0.3
|
Bal.
|
기계적 특성
|
이름
|
값
|
|
내마모성
|
우수한
|
|
부식 저항
|
좋은
|
|
전형적인 경도
|
HRC 40-45
|
|
본드 강도
|
7100 psi
|
|
증착 비율
|
10 lbs / hr / 100A
|
|
증착 효율성
|
70 %
|
|
와이어 커버리지
|
0.8 oz / ft2 / mil
|
|
코팅 수축
|
낮은 평가
|
|
서비스 온도
|
550C/1022 F까지
|
크기 및 포장
|
조건
|
솔리드 와이어
|
|
지름
|
1.6mm (14ga), 2.0mm, 3.175mm
|
|
패키지 크기
|
10kg, 15kg 또는 고객의 요구에 따라
|